| Customization: | Available |
|---|---|
| Certification: | CE, FDA, ISO, PCI, PDA, UR |
| Condition: | New |
| Shipping Cost: | Contact the supplier about freight and estimated delivery time. |
|---|
| Payment Methods: |
|
|---|---|
| Support payments in USD |
| Secure payments: | Every payment you make on Made-in-China.com is protected by the platform. |
|---|
| Refund policy: | Claim a refund if your order doesn't ship, is missing, or arrives with product issues. |
|---|
Suppliers with verified business licenses
Audited Supplier Audited by an independent third-party inspection agency
| Item | TEST ITEMS | MEASURED VALUE | |
| BL002 BL007 BL008 | Base(Com A) | Appearance | White /Grey Ropy Paste |
| Density | 1.41g/cm3 | ||
| Viscosity | 170,000 mPa.S | ||
| Catalyst(Com B) | Appearance | Black/White Ropy Paste | |
| Density | 1.03 g/cm3 | ||
| Viscosity | 80,000 mPa.S | ||
| As mixed | |||
| Mixture By weight(A:B=12:1) | Appearance | Black/White/Grey | |
| Density | 1.40g/cm3 | ||
| Viscosity | 340,000 mPa.S | ||
| Application Time(23ºC.50%) | 30~50 mins | ||
| Tack-free Time(23ºC,50%) | 30~60 mins | ||
| Sag | Placed Vertical (50ºC) | 0 | |
| Placed Horizontal | No deformation | ||
| Hardness | Shore A- 24h | 35 | |
| Shore A-14 days | 44 | ||
| As cured -After 14 days at T 23ºC and 50% RH. | |||
| Tensile Adhesion Strength | 23ºC | 0.97 MPa | |
| 90ºC | 0.85 MPa | ||
| -30ºC | 1.84MPa | ||
| AfterAging in Hot Air | 1.01 MPa | ||
| After Water-UV Immersion | 0.97 MPa | ||
| Adhesive Failure Area | 0 | ||
| 23ºC Elongation Under Max.Tensile Strength | 1.4 | ||
| Temperature Resistance | -60%~180ºC | ||
| Resistance to UV-Ozone | UV2500 hrs,No change | ||
| Moisture Vapour Transmission Rate (MVTR) | 17.7 [gr/m2.24hrs.2mm]-EN1279/4 | ||
| Gas Permeation Rate(Ar) | 755x103lgr/m2hrsl.EN1279/4 | ||